陶瓷墙地砖成形缺陷的探讨
陶瓷墙地砖成形缺陷的探讨
摘要:陶瓷墙地砖的干压成形工艺由于具有方法简单,容易实现自动化等特点,在生产中得到了广泛的应用,但在压制成形过程中会存在许多缺陷,直接影响着产品的质量,文中就一些常见的由于设备原因引起的缺陷,作一探索性的分析,以便找出原因,及时调整,制定克服办法,最大限度地降低半成品缺陷,提高产品合格率,从而提高企业效益。
关键词:陶瓷墙地砖;压制;缺陷;原因;解决办法
Abstract: the dry pressing ceramic tiles forming process has the method is simple and easy to realize the automation and other characteristics, in the production of a wide range of applications, but in the press forming process has many defects, the direct impact on the quality of the products, in some of the common causes of defects of the equipment, and make a tentative analysis, so as to find out the cause, adjust in time, make to overcome, maximize reduce defects semi-finished products, improve the quality, so as to improve the enterprise benefit.
Keywords: Wall and floor tiles; suppress; fault, Reason; solution
1前言
陶瓷墙地砖(又称玻化砖)作为新一代陶瓷地砖,以其耐磨、耐腐蚀,色泽艳丽、仿天然石材、环保等优点深受消费者的喜爱。
因玻化砖属于完全烧结材料,所以在生产过程中容易出现各种各样的产品质量缺陷,如砖坯大小头、厚度偏差、凹凸边、变形、分层、开裂等。而大型压机,以生产600mm×600mm 、800mm×800mm 大规格产品为主,通过几年来不断地探索,已找到解决上述问题的思路及办法,本文主要从设备对成形砖坏角度分析探讨各种缺陷的形成原因及其解决办法。
大小头
陶瓷墙地砖产品质量缺陷之一就是砖坯经烧成后,砖块的对边尺寸不均等,超过控制的偏差值。所谓大小头,即出窑砖坯尺寸偏差值超过标准要求,一般来说,偏差值应控制在规格尺寸的0.4%以内。大小头缺陷在玻化砖生产中是最容易出现又较难解决的一个问题,其形成的主要原因是粉料压制后坯体致密分布不均,在烧成后收缩不一致所造成的。影响坯体致密分布不均有以下因素:
2.1 压机冲压前喂料车布料不均匀