不锈钢焊丝国家标准[GB4242-84]

不锈钢焊丝

（1）中国YB标准不锈钢焊丝[YB/T 5092-1993] YB标准不锈钢焊丝的牌号与化学成分，见表8-1-47。

表8-1-47 不锈钢焊丝的牌号与化学成分（质量分数）（%）

P

焊丝牌号

C

Si

Mn

≤

S

Cr

≤

Ni

Mo

其他

铁素体型

H0Cr14 H1Cr17

≤0.06 0.30-0.70 0.30-0.70 ≤0.030 ≤0.030 13.00-15.00 ≤0.10

≤0.50

≤0.60

≤0.030 ≤0.030 15.50-17.00

马氏体型

H1Cr13 H1Cr5Mo

≤0.12

≤0.50

≤0.60

≤0.030 ≤0.030 11.50-13.50

4.00-6.00

— ≤3.00

— 0.40-0.60

— —

≤6.00 —

— —

— —

≤0.12 0.15-0.35 0.40-0.70 ≤0.030 ≤0.030

奥氏体型

H0Cr21Ni10 H00Cr21Ni10

≤0.06 ≤0.03

≤0.60 ≤0.60

1.00-2.50 ≤0.030 ≤0.030 19.50-22.00 9.00-11.00 1.00-2.50 ≤0.030 ≤0.030 19.50-22.00 9.00-11.00

— —

— —

H1Cr24Ni13 ≤0.12 ≤0.60 1.00-2.50 ≤0.030 ≤0.030 23.00-25.00 12.00-14.00 — —

H1Cr24Ni13Mo2 H0Cr26Ni21 H0Cr26Ni21 H0Cr19Ni12Mo2 H00Cr19Ni12Mo2

≤0.12 ≤0.60 1.00-2.50 ≤0.030 ≤0.030 23.00-25.00 12.00-14.00 2.00-3.00

— —

— — — — — Cu1.00-2.50

— Ti9×C%-1.00 Nb10×C%-1.00

≤0.15 0.2-0.59 1.00-2.50 ≤0.030 ≤0.030 25.00-28.00 20.00-22.50 ≤0.08 ≤0.08 ≤0.03

≤0.06 ≤0.60 ≤0.60 ≤0.60 ≤0.60 ≤0.60 ≤0.60

1.00-2.50 ≤0.030 ≤0.030 25.00-28.00 20.00-22.50

1.00-2.50 ≤0.030 ≤0.030 18.00-20.00 11.00-14.00 2.00-3.00 1.00-2.50 ≤0.030 ≤0.030 18.00-20.00 11.00-14.00 2.00-3.00 1.00-2.50 ≤0.030 ≤0.030 18.00-20.00 11.00-14.00 2.00-3.00 1.00-2.50 ≤0.030 ≤0.030 18.50-20.50 13.00-15.00 3.00-4.00 1.00-2.50 ≤0.030 ≤0.030 18.50-20.50 9.00-10.50 1.00-2.50 ≤0.030 ≤0.030 19.00-2.50

9.00-11.00

— —

H00Cr19Ni12Mo2Cu2 ≤0.03 H0Cr20Ni14Mo3 H0Cr20Ni10Ti H0Cr20Ni10Nb

≤0.06 ≤0.06 ≤0.08

H1Cr21Ni10Mn6 ≤0.10 0.20-0.60 5.00-7.00 ≤0.030 ≤0.030 20.00-22.00 9.00-11.00 — —

注：国家标准[GB4242-84己调整为YB/T行业标准。 （2）中国GB标准埋弧用不锈钢焊丝[GB/T17854-1999] a.GB标准埋弧用不锈钢焊丝的牌号与化学成分，见表8-1-48。

表8-1-48 准埋弧用不锈钢焊丝的牌号与化学成分（质量分数）（%）

焊丝牌号 H0Cr21Ni10 H00Cr21Ni10 H1Cr24Ni13 H1Cr24Ni13Mo2 H1Cr26Ni21 H0Cr19Ni12Mo2 H00Cr19Ni12Mo

C Si Mn P S Cr Ni Mo — — —

其他 — — — — — — — Cu1.00-2.50

— Nb10×C%-1.00

— —

≤0.08 ≤0.60 1.00-2.50 0.030 0.030 19.50-22.00 9.00-11.00 ≤0.03 ≤0.60 1.00-2.50 0.030 0.020 19.50-22.00 9.00-11.00 ≤0.12 ≤0.60 1.00-2.50 0.030 0.030 23.00-25.00 12.00-14.00

≤0.12 ≤0.60 1.00-2.50 0.030 0.030 23.00-25.00 12.00-14.00 2.00-3.00 ≤0.15 ≤0.60 1.00-2.50 0.030 0.030 25.00-28.00 20.00-22.00

—

≤0.08 ≤0.60 1.00-2.50 0.030 0.030 18.00-20.00 11.00-14.00 2.00-3.00 ≤0.03 ≤0.60 1.00-2.50 0.030 0.020 18.00-20.00 11.00-14.00 2.00-3.00

H00Cr19Ni12Mo2Cu2 ≤0.03 ≤0.60 1.00-2.50 0.030 0.020 18.00-20.00 11.00-14.00 2.00-3.00 H0Cr19Ni14Mo3 H0Cr20Ni10Nb

H1Cr13 H1Cr17

≤0.08 ≤0.60 1.00-2.50 0.030 0.030 18.50-20.50 13.00-15.00 3.00-4.00 ≤0.08 ≤0.60 1.00-2.50 0.030 0.030 19.00-21.50 9.00-11.00 ≤0.12 ≤0.50 ≤0.10 ≤0.50

≤0.60 ≤0.60

0.030 0.030 11.50-13.50 0.030 0.030 15.50-17.50

≤0.60 ≤0.60

— — —

注：根据供需双方协议，也可生产本表牌号以外的焊丝。

b.GB标准埋弧用不锈钢焊丝和焊剂组合的熔敷金属的化学成分，见表8-1-49。

表8-1-49 埋弧用不锈钢焊丝和焊剂组合的熔敷金属的化学成分（质量分数）（%）

焊丝和焊剂型号 F308-H××× F308L-H××× F309-H××× F309Mo-H×××

C ≤0.08 ≤0.04 ≤0.15 ≤0.12

Si Mn P S Cr Ni Mo — — —

其他 — — — —

≤1.00 0.50-2.50 0.040 0.030 18.0-21.0 9.0-11.0 ≤1.00 0.50-2.50 0.040 0.030 18.0-21.0 9.0-11.0 ≤1.00 0.50-2.50 0.040 0.030 22.0-25.0 12.0-14.0

≤1.00 0.50-2.50 0.040 0.030 22.0-25.0 12.0-14.0 2.00-3.00

F310-H××× F316-H××× F316L-H××× F316CuL-H××× F317-H××× F347-H××× F410H-××× F430-H×××

≤0.20 ≤0.08 ≤0.04 ≤0.04 ≤0.08 ≤0.08 ≤0.12 ≤0.10

≤1.00 0.50-2.50 0.030 0.030 25.0-28.0 20.0-22.0 — — — — Cu1.00-2.50

— Nb8×C%-1.00

— —

≤1.00 0.50-2.50 0.040 0.030 17.0-20.0 11.0-14.0 2.00-3.00 ≤1.00 0.50-2.50 0.040 0.030 17.0-20.0 11.0-14.0 2.00-3.00 ≤1.00 0.50-2.50 0.040 0.030 17.0-20.0 11.0-14.0 1.20-2.75 ≤1.00 0.50-2.50 0.040 0.030 18.0-21.0 12.0-14.0 3.00-4.00 ≤1.00 0.50-2.50 0.040 0.030 18.0-21.0 9.0-11.0 ≤1.00 ≤1.00

≤1.20 ≤1.20

0.040 0.030 11.0-13.5 0.040 0.030 15.0-18.0

≤0.60 ≤0.60

— — —

注：焊剂型号中添加字母L的，表示较低碳含量。

c.GB标准埋弧焊用不锈钢焊丝和焊剂组合的熔敷金属的力学性能，见表8-1-50。 表8-1-50 埋弧焊用不锈钢焊丝和焊剂组合的熔敷金属的力学性能

抗拉强度σb/MPa

焊丝和焊剂型号

伸长率δ(%)

焊丝和焊剂型号

抗拉强度σb/MPa 伸长率δ(%)

（不小于）

F308-H××× F308L-H××× F309-H××× F309Mo-H××× F310-H×××① F316-H×××②

520 480 520 550 520 520

30 25 25 25 25 25

F316L-H××× F316CuL-H××× F317-H××× F347-H××× F410H-××× F430-H×××

480 480 520 520 440 450

（不小于）

30 30 25 25 20 17

①试样加工前经840-870℃保温2h，以小于55℃/h的冷却速度炉冷至590℃，随后空冷。 ②试样加工前经760-785℃保温2h，以小于55℃/h的冷却速度炉冷至590℃，随后空冷。 （3）中国GB标准不锈钢药芯焊丝[GB/T 17853-1999]

a.GB标准不锈钢药芯焊丝的型号与熔敷金属的化学成分，见表8-1-51。

表8-1-51 不锈钢药芯焊丝的型号与熔敷金属的化学成分（质量分数）（%）

型号 C Si Mn

P S

Cr Ni Mo 其他

≤ ≤

E307T×-× E308T×-× E308LT×-× E308HT×-× E308MoT×-× E308LMoT×-× E309T×-×

≤0.13 ≤0.08 ≤0.04 0.04-0.08 ≤0.08 ≤0.04 ≤0.10

≤1.00 ≤1.00 ≤1.00 ≤1.00 ≤1.00 ≤1.00 ≤1.00

3.30-4.75 0.040 0.030 18.0-20.5 9.00-10.5 0.50-1.50 ≤0.50 ≤0.50 ≤0.50 2.00-3.00 2.00-3.00 ≤0.50

Cu≤0.50 Cu≤0.50 Cu≤0.50 Cu≤0.50 Cu≤0.50 Cu≤0.50 Cu≤0.50 Nb0.70-1.00

0.50-2.50 0.04 0.030 18.0-21.0 9.00-11.00 0.50-2.50 0.040 0.030 18.0-21.0 9.00-11.00 0.50-2.50 0.040 0.030 18.0-21.0 19.00-11.00 0.50-2.50 0.040 0.030 18.0-21.0 0.50-2.50 0.040 0.030 18.0-21.0 0.50-2.50 0.040 0.030 22.0-25.0

9.00-11.0 9.00-12.0 12.0-14.0

E309LNbT×-× ≤0.04 ≤1.00 0.50-2.50 0.040 0.030 22.0-25.0 12.0-14.0 ≤0.50

Cu≤0.50

E309LT×-× E309MoT×-× E309LMoT×-× E309LNiMoT×-× E310T×-× E312T×-× E316T×-× E316LT×-× E317LT×-×

≤0.04 ≤0.12 ≤0.04 ≤0.04 ≤0.20 ≤0.15 ≤0.08 ≤0.04 ≤0.04

≤1.00 ≤1.00 ≤1.00 1.00 ≤1.00 ≤1.00 ≤1.00 ≤1.00 ≤1.00

0.50-2.50 0.040 0.030 22.0-25.0 0.50-2.50 0.040 0.030 21.0-25.0 0.50-2.50 0.040 0.030 21.0-25.0 0.50-2.50 0.040 0.030 20.5-23.5 1.00-2.50 0.030 0.030 25.0-28.0 0.50-2.50 0.030 0.030 28.0-32.0 0.50-2.50 0.040 0.030 17.0-20.0 0.50-2.50 0.040 0.030 17.0-20.0 0.50-2.50 0.040 0.030 18.0-21.0

12.0-14.0 12.0-16.0 12.0-16.0 15.0-17.0 20.0-22.5 8.00-10.5 11.0-14.0 11.0-14.0 12.0-14.0

≤0.50 2.00-3.00 2.00-3.00 2.50-3.50 ≤0.50 ≤0.50 2.00-3.00 2.00-3.00 3.00-4.00

Cu≤0.50 Cu≤0.50 Cu≤0.50 Cu≤0.50 Cu≤0.50 Cu≤0.50 Cu≤0.50 Cu≤0.50 Cu≤0.50 Nb8×C-1.00

E347T×-× ≤0.08 ≤1.00 0.50-2.50 0.040 0.030 18.0-21.0 9.00-11.0 ≤0.50

Cu≤0.50 Ti 10×C-1.50

E409T×-× ≤0.10 ≤1.00 ≤0.80 0.040 0.030 10.5-13.5 ≤0.60 ≤0.50

Cu≤0.50

E410T×-× E410N1MoT×-×

≤0.12 ≤0.06

≤1.00 ≤1.00

≤1.20 ≤1.00

0.040 0.030 11.0-13.5 0.040 0.030 11.0-12.5

≤0.60 4.00-5.00

≤0.50 0.40-0.70

Cu≤0.50 Cu≤0.50 Ti 10×C-1.50

E410NiTiT×-× ≤0.04 ≤0.50 ≤0.70 0.030 0.030 11.0-12.0 3.60-4.50 ≤0.50

Cu≤0.50

E430T×-× E502T×-× E505T×-× E307T0-3 E308T0-3 E308LT0-3 E308HT0-3 E308MoT0-3 E308LMoT0-3 E308HMoT0-3 E309T0-3 E309LT0-3

≤0.10 ≤0.10 ≤0.10 ≤0.13 ≤0.08 ≤0.03 0.04-0.08 ≤0.08 ≤0.03

≤1.00 ≤1.00 ≤1.00 ≤1.00 ≤1.00 ≤1.00 ≤1.00 ≤1.00 ≤1.00

≤1.20 ≤1.20 ≤1.20

0.040 0.030 15.0-18.0 0.040 0.030 4.00-6.00 0.040 0.030 8.00-10.5

≤0.60 ≤0.40 ≤0.40 9.00-10.5 9.00-11.0 9.00-11.0 9.00-11.0 9.00-11.0 9.00-12.0 9.00-10.7 12.0-14.0 12.0-14.0

≤0.50 0.45-0.65 0.85-1.20 0.50-1.50 ≤0.50 ≤0.50 ≤0.50 2.00-3.00 2.00-3.00 1.80-2.40 ≤0.50 ≤0.50

Cu≤0.50 Cu≤0.50 Cu≤0.50 Cu≤0.50 Cu≤0.50 Cu≤0.50 Cu≤0.50 Cu≤0.50 Cu≤0.50 Cu≤0.50 Cu≤0.50 Cu≤0.50 Nb0.70-1.00

3.30-4.75 0.040 0.030 19.5-22.0 0.50-2.50 0.040 0.030 19.5-22.0 0.50-2.50 0.040 0.030 19.5-22.0 0.50-2.50 0.040 0.030 19.5-22.0 0.50-2.50 0.040 0.030 18.0-21.0 0.50-2.50 0.040 0.030 18.0-21.0

0.07-0.12 0.25-0.80 1.25-2.50 0.040 0.030 19.0-21.5 ≤0.10 ≤0.03

≤1.00 ≤1.00

0.50-2.50 0.040 0.030 23.0-25.5 0.50-2.50 0.040 0.030 23.0-25.5

E309LNbT0-3 ≤0.03 ≤1.00 0.50-2.50 0.040 0.030 23.0-25.5 12.0-14.0 ≤0.50

Cu≤0.50

E309MoT0-3 E309LMoT0-3 E310T0-3 E312T0-3 E316T0-3 E316LT0-3 E316LKT0-3 E317LT0-3

≤0.12 ≤0.04 ≤0.20 ≤0.15 ≤0.08 ≤0.03 ≤0.04 ≤0.03

≤1.00 ≤1.00 ≤1.00 ≤1.00 ≤1.00 ≤1.00 ≤1.00 ≤1.00

0.50-2.50 0.040 0.030 21.0-25.0 0.50-2.50 0.040 0.030 21.0-25.0 1.00-2.50 0.030 0.030 25.0-28.0 0.50-2.50 0.040 0.030 28.0-32.0 0.50-2.50 0.040 0.030 18.0-20.5 0.50-2.50 0.040 0.030 18.0-20.5 0.50-2.50 0.040 0.030 17.0-20.0 0.50-2.50 0.040 0.030 18.5-21.0

12.0-16.0 12.0-16.0 20.0-22.5 8.00-10.5 11.0-14.0 11.0-14.0 11.0-14.0 13.0-15.0

2.00-3.00 2.00-3.00 ≤0.50 ≤0.50 2.00-3.00 2.00-3.00 2.00-3.00 13.00-14.00

Cu≤0.50 Cu≤0.50 Cu≤0.50 Cu≤0.50 Cu≤0.50 Cu≤0.50 Cu≤0.50 Cu≤0.50 Nb8×C-1.00

E347T0-3 ≤0.08 ≤1.00 0.50-2.50 0.040 0.030 19.0-21.5 9.00-11.0 ≤0.50

Cu≤0.50 Nb10×C-1.50

E409T0-3 ≤0.10 ≤1.00 ≤0.80 0.040 0.030 10.5-13.5 ≤0.60 ≤0.50

Cu≤0.50

E410T0-3 E410NiMoT0-3

≤0.12 ≤0.06

≤1.00 ≤1.00

≤1.00 ≤1.00

0.040 0.030 11.0-13.5 0.040 0.030 11.0-12.5

≤0.60 4.0-5.00

≤0.50 0.40-0.70

Cu≤0.50 Cu≤0.50

Nb10×C-1.50

E410NiTiT0-3

≤0.04

≤0.50

≤0.70

0.030 0.030 11.0-12.0

3.60-4.50

≤0.50

Cu≤0.50

E430T0-3 E2209T0-× E2553T0-× E×××T×-G R308LT1-5 R309LT1-5 R316LT1-5

≤0.10 ≤0.04 ≤0.04 — ≤0.03 ≤0.03 ≤0.03

≤1.00 ≤1.00 ≤0.75 — ≤1.20 ≤1.20 ≤1.20

≤1.00

0.040 0.030 15.0-18.0

≤0.60

≤0.50 2.50-4.00 2.90-3.90

— ≤0.05 ≤0.50 2.00-3.00

Cu≤0.50 Cu≤0.50 Cu1.50-2.50

— Cu≤0.50 Cu≤0.50 Cu≤0.50 Nb8×C-1.00

R347T1-5

≤0.08

≤1.20

0.50-2.50 0.040 0.030 18.0-21.0

9.00-11.0

≤0.50

Cu≤0.50

0.50-2.00 0.040 0.030 21.0-24.0 17.50-10.0 0.50-1.50 0.040 0.030 24.0-27.0

—

—

—

—

8.50-10.0

— 9.00-11.0 12.0-14.0 11.0-14.0

0.50-2.50 0.040 0.030 18.0-21.0 0.50-2.50 0.040 0.030 22.0-25.0 0.50-2.50 0.040 0.030 17.0-20.0

注：1.当对表中给出的元素进行化学分析时，若存在其他元素（铁除外），由其总量（质量分数）不得超过0.50%。 2.表中Nb含量为Nb+Ta含量。 3.E×××T×-G的化学成分不规定。

b.GB标准不锈钢药芯焊丝熔敷金属的力学性能，见表8-1-52.

表8-1-52 不锈钢药芯焊丝熔敷金属的力学性能

抗拉强度σb/MPa

型号

（不小于）

E307T×-× E308T×-× E308LT×-× E308HT×-× E308MoT×-× E308LMoT×-× E309T×-× E309LNbT×-× E309LT×-×

590 550 520 550 550 520 550 520 520

伸长率δ（%）

热处理

30 35 35 35 35 35 25 25 25

— — — — — — — — —

E309MoT×-× E309LMoT×-× E309LNiMoT×-× E310T×-× E312T×-× E316T×-× E316LT×-× E317LT×-× E347T×-× E409T×-× E410T×-× E410N1MoT×-× E410NiTiT×-× E430T×-× E502T×-× E505T×-× E308HMoT0-3 E316LKT0-3 E2209T0-× E2553T0-× E×××T×-G R308LT1-5 R309LT1-5 R316LT1-5 R347T1-5

550 520 520 550 660 520 485 520 520 450 520 760 760 450 415 415 550 485 690 760 — 520 520 785 520

25 25 25 25 22 30 30 20 25 15 20 15 15 20 20 20 30 30 20 15 — 35 30 30 30

— — — — — — — — — — — b) b) c) d) d) — — — — — — — — —

注：热处理栏的字母表示不同的热处理制度。

a)试样加热到730-760℃保温1h后，以小于55℃/h的冷却速度炉冷至315℃，出炉空冷至室温。 b)试样加热到595-620℃保温1h后，出炉空冷至室温。

c)试样加热到760-790℃保温4h后，以小于55℃/h的冷却速度炉冷至590℃，出炉空冷至室温。 d)试样加热到840-870℃保温2h后，以小于55℃/h的冷却速度炉冷至315℃，出炉空冷至室温。